Blue paint suitable for Goweil technique RAL5010

High resistance to UV and weather conditions
Very easy to work with, high final hardness, lasting gloss
Chrome and lead free
Advantages
Long service life
Effective work
Low environmental impact
Application
Surface treatment for use in the industrial sector, tractors, agricultural machinery and civil engineering machinery
Iron and steel
Resistant to gasoline and diesel for short-term contact

Binder base: modified alkyd resins
dry solids: 52-58%
Base viscosity (DIN 53 211): thixotropic
Specific gravity (DIN 51 757): 0.97-1.18 kg/l
Gloss level (DIN 67 530) 80%/60° (high gloss)
Temperature resistance: continuous load 130°C, short-term load 150°C
Conditions of use: from +10°C and up to 80% relative humidity
Set to touch after 6-8 hours (at 20°C)
Cures after 24 hours (at 20°C)
Final hardness after 3-4 days (at 20°C)
Base layer: Kramp primer (layer thickness: 50-60 µm)
Top layer: Kramp synthetic resin varnish (layer thickness: 50-60 µm)
Theoretical coverage per liter: 7.5-8.0 m²/kg (with a layer thickness of 50 µm)

Surface preparation: The object to be processed must be thoroughly cleaned, degreased and, if necessary, polished
Some types are semi-gloss and matte
Conforms to the Austrian Solvent Ordinance (01/01/96)
Drying time can be shortened by using Kramp quick drying thinners instead of Kramp synthetic resin thinners
Lower temperatures result in longer drying times